Polycoat II
Product Data Sheet
| | | |
| Description | AN INTERIOR/EXTERIOR PIGMENTED ACRYLIC URETHANE TWO COMPONENT ENAMEL |
759101x White Base
759102x Midtone Base
759103x Deeptone Base
759104x Neutral Base
759106x Clear Base | |
|
| Basic Use | Polyurethane, two component high gloss coating that combines the appearance of a high quality enamel and the performance of a chemically cured coating. Polycoat II protects metal surfaces in marine enviroments, chemical plants and other corrosive areas. |
| |
| Pot Life | 4 hours at 77 degrees F. | Components | 4:1 mix ratio with Product 28004 for Part B |
| Shelf Life | 2+ years unopened 40-90 Deg F | | |
| Induction | No induction time is required | Mixing Instructions | Premix Part A to insure all material is in suspension, then add Part B. |
Properties
| | | | | |
| VOC gr/L | 520.00 | Volume Solids ±2% | 43.30 | Odor | Ketone/aromatic |
| VOC lbs/G | 4.34 | Weight Solids ±2% | 56.70 | Thinning | If, 10% 799260 synth rdcr |
| |
| MPI # | 78 | Theor. Spread Rate | 400.0 | Weight | 10.00 |
| Gloss 60° | 90-105 | Wet Film Thickness | 3.5 mils | Viscosity | 60 - 66 Krebs Units |
| Sheen 85° | | Dry Film Thickness | 1.5 mils | Resistance | water & chemical resistance |
| |
| Tinting Type | | Toxic Properties | None as dry film | Cleanup | MIBK |
| Local Harvest | | Light Reflectance | Will vary with color | Packaging | As desired |
| |
| | | | | |
| |
| | | | | |
| |
| |
| |
| |
| |
| |
| |
| |
| |
| |
Dry Times
At 77 degrees Fahrenheit and 50% Relative Humidity.
| | | | | |
| Dry To Touch | 1/2 hour to 1 hour | Dry To Sand | N/A | Tack Free | 1/2 hour |
| Dry To Recoat | 12 hours | Dry To Topcoat | 12 hours | Dry To Hard | 12 hours |
Prep & Prime
Surfaces must be clean, dry, and free of contaminants such as wax, oils, grease, weld splatter, or loose mil/scale/rust. As a minimum, SSPC-SPC Hand Tool Cleaning or SSPC-SPC3 Machine Tool Cleaning is recommended. Smooth surfaces should be abraded to enhance adhesion. Improved performance can be achieved with SSPC-SPC Commercial Blast. All surfaces prepared for painting should be coated within 8 hours of completion of surface prep.
| |
| |
| Masonry | May be used satisfactorily on these surfaces when proper surface preparation and priming is completed. |
| Metal | Non-Ferrous: Must be treated with Galvprep or similar type etching material.
Ferrous: Must have all mill scale, rust, dirt, grease,etc., removed. Prime with a suitable primer such as Barrier III, Barrier III HS, Ropon, or Ropn HS Primer prior to topcoating. |
| |
| |
| |
Application
Spray Application recommended. May be brushed or rolled.
CONDITIONS: Do not apply when surface temps are expected to drop below 40 degrees F. or rise above 95 degrees F. during application and drying. Surface temperature must be at least 50 degrees F. above dew point. Do not apply to surfaces which will be exposed to rain or moisture before coating is dry.
| |
| Coats | One or more depending on desired dry film thickness. |
| Brush | Use a natural bristle brush. |
| Roller / Pad | Use 3/16" to 3/8" nap synthetic or lambswool roller cover. Use a synthetic pad. |
| Airless Spray | Recommend pressure 2000 to 2500 psi, Use a .013" to .016" tip orifice. |
| |
| Conventional Spray | Recommended air pressure 40 - 60 psi; fluid pressure 20 psi; JGA 510 gun, FX tip, 705 air cap. |
Corporate: 6107 N Marine Drive Portland, Oregon 97203 - Rodda Paint Co. - Regional: 3838 4th Avenue South Seattle, Washington 98134
Disclaimer - All technical advice, recommendations and services regarding this product are rendered by the Seller gratis. They are based on technical data which the Seller believes to be reliable and are intended for use by persons having skill and know-how, at their discretion and risk. Seller assumes no responsibility for results obtained or damages incurred from this product use by Buyer whether as recommended herein or otherwise. Such recommendations, technical advice or services are not to be taken as a license to operate under or suggest infringement of any patent.
Last Modification Date: 6/1/2011 - Please contact us at 800.452.2315 for additional information or questions