Hi Solids Equipment Enamel
Product Data Sheet
Properties
| | | | | |
| VOC gr/L | 414.00 | Volume Solids ±2% | 50.60 | Odor | Dominant of paint thinner |
| VOC lbs/G | 3.45 | Weight Solids ±2% | 67.10 | Thinning | Do not thin. |
| |
| MPI # | | Theor. Spread Rate | 275.0 | Weight | 10.40 |
| Gloss 60° | 85-100 | Wet Film Thickness | 5 - 6 mils | Viscosity | 60 - 65 Krebs Units |
| Sheen 85° | | Dry Film Thickness | 2.5 - 3 mils | Resistance | Excellent |
| |
| Tinting Type | Industrial | Toxic Properties | Non-toxic a dry film | Cleanup | 799260x Synthetic Reducer |
| Local Harvest | | Light Reflectance | white 88%, less on tints | Packaging | single & five gallons |
| |
| | | | | |
| |
| | | | | |
| |
| |
| |
| |
| |
| |
| |
| |
| |
| |
Dry Times
At 77 degrees Fahrenheit and 50% Relative Humidity.
| | | | | |
| Dry To Touch | 2 hours | Dry To Sand | N/A | Tack Free | 8 |
| Dry To Recoat | 12 hours | Dry To Topcoat | | Dry To Hard | 48 hours |
Prep & Prime
Surfaces must be clean, dry and free of contaminants such as wax, oils, grease, weld splatter, or loose mil/scale/rust. As a minimum, SSPC-SPC Hand Tool Cleaning or SSPC-SPC3 Machine Tool Cleaning is recommended. Smooth surfaces should be abraded to enhance adhesion. Improved performance can be achieved with SSPC-Sp6 Commercial Blast. All surfaces prepared for painting should be coated within 8 hours of completion of surface prep.
| |
| |
| Masonry | Not recommended for these surfaces, but may be used satisfactorily over previous coated surfaces. Bare areas must be primed with 501601x First Coat Primer. |
| Metal | New metal should be thoroughly cleaned before coating. For optimum corrosion and erosion resistance, prime with 7082xxx Barrier III High Solids Metal Primer. |
| |
| Wood | Not recommended for these surfaces, but may be used satisfactoily over previously coated surfaces. Bare areas must be primed with 501601x First Coat Primer. |
| |
Application
Do not apply when air or surface temepratures are expected to drop below 50 degrees F. or rise above 95 degrees F. during application and drying. Spray application recommended, may be brushed or rolled on small areas.
| |
| Coats | One or more depending on desired dry film thickness. |
| Brush | Small items may be brushed. Natural bristle 3 to 4 inch brush. Apply with full strokes. Avoid rebrushing until paint is dry. |
| Roller / Pad | Small areas, use top quality polyester cover. |
| Airless Spray | Recommend pressure 200 to 2500 psi, using .013 to .017 tip orifice. |
| HVLP | Use approximately five pounds fluid and ten pounds atomizing air. |
| |
Corporate: 6107 N Marine Drive Portland, Oregon 97203 - Rodda Paint Co. - Regional: 3838 4th Avenue South Seattle, Washington 98134
Disclaimer - All technical advice, recommendations and services regarding this product are rendered by the Seller gratis. They are based on technical data which the Seller believes to be reliable and are intended for use by persons having skill and know-how, at their discretion and risk. Seller assumes no responsibility for results obtained or damages incurred from this product use by Buyer whether as recommended herein or otherwise. Such recommendations, technical advice or services are not to be taken as a license to operate under or suggest infringement of any patent.
Last Modification Date: 6/20/2011 - Please contact us at 800.452.2315 for additional information or questions